MgO（氧化镁）

氧化镁可用于高温窗口和基材。 HTSC 基材。

物理与光学性质

Transmission Range :	0.3 to 6 μm
Refractive Index :	1.7085 at 2 μm (1)
Reflection Loss :	12.8% at 2 μm (2 surfaces)
Absorption Coefficient :	0.05 cm-1 at 5.5 μm
Reststrahlen Peak :	n/a
dn/dT :	+19 x 10-6 /°C
dn/dμ = 0 :	n/a
Density :	3.58 g/cc
Melting Point :	2800 °C
Thermal Conductivity :	42 W m-1 K-1 at 273K
Thermal Expansion :	10.8 x 10-6 /°C at 273K
Hardness :	Knoop 692 with 600g indenter
Specific Heat Capacity :	877 J Kg-1 K-1
Dielectric Constant :	9.65 at 1 MHz
Youngs Modulus (E) :	249 GPa
Shear Modulus (G) :	155 GPa
Bulk Modulus (K) :	155 GPa
Elastic Coefficients :	C11=294; C12=93; C44=155
Apparent Elastic Limit :	138 MPA (20,000 psi)
Poisson Ratio :	0.18
Solubility :	0.00062g/100g Water
Molecular Weight :	40.32
Class/Structure :	Cubic FCC, NaCl, Fm3m, (100) cleavage

 

 

折射率

 

No = 寻常光

µm	No	µm	No	µm	No
0.171	2.319	0.180	2.138	0.191	2.039
0.200	1.986	0.230	1.892	0.276	1.824
0.310	1.795	0.382	1.7668	0.436	1.75471
0.50	1.754	0.644	1.734	1.00	1.7229
2.00	1.7085	3.00	1.6915	4.00	1.6679
5.00	1.6373	6.02	1.5957	7.04	1.543
8.07	1.475	9.09	1.389	10.64	1.209

 

 

产品说明

氧化镁的生产规模相对较小，主要产地为日本和中国。

Tags: MgO（氧化镁）

---