二氧化钛（金红石型）

金红石是一种用于耦合棱镜的高折射率材料。

 

物理与光学性质

Transmission Range :	0.43 to 5.0 μm
Refractive Index :	No 2.555 at 0.69μ (1)(2)
Reflection Loss :	30% at 2μ (2 surfaces)
Absorption Coefficient :	n/a
Reststrahlen Peak :	n/a
dn/dT :	n/a
dn/dμ = 0 :	2.81μ
Density :	4.26 g/cc
Melting Point :	1840 °C
Thermal Conductivity :	12.5 (para) 8.7 (perp) W m-1 K-1
Thermal Expansion :	9.2 (para) 7.1 (perp) x 10-6 /°C
Hardness :	Knoop 879 with 500g indenter
Specific Heat Capacity :	711 J kg-1 K-1
Dielectric Constant :	160 at 1 MHz
Youngs Modulus (E) :	n/a
Shear Modulus (G) :	n/a
Bulk Modulus (K) :	n/a
Elastic Coefficients :	C11=269;C12=177;C13=146;C33=480;C44=124
Apparent Elastic Limit :	4.8 MPa (700 psi)
Poisson Ratio :	0.28
Solubility :	Insoluble in water
Molecular Weight :	79.9
Class/Structure :	Tetragonal, SnO2 rutile, P4/mmm

 

折射率 

No = 寻常光         Ne = 非常光

µm	No	Ne	µm	No	Ne	µm	No	Ne
0.436	2.853	3.216	0.492	2.725	3.051	0.496	2.718	3.042
0.546	2.652	2.958	0.577	2.623	2.921	0.579	2.621	2.919
0.589	2.616	2.903	0.691	2.555	2.836	0.708	2.548	2.826
1.01	2.484	2.747	1.530	2.454	2.710	2.42	2.40	2.59
3.38	2.41	2.58	3.79	2.39	2.57	4.28	2.34	2.51
4.89	2.32	2.49	5.73	2.24	2.43

 

产品说明

金红石采用切克劳斯基法（Czochralski method）生长，直径可达 25 mm，长度可达 80 mm。

Tags: 二氧化钛（金红石型）

---